提高20t电弧炉炉衬寿命工艺实践

炉渣碱度、泡沫渣高度、吹氧角度、补炉方式等是影响20t电弧炉炉衬寿命的主要因素。为了提高炉衬寿命,莱钢炼钢厂采取了控制炉渣组成、泡沫渣全程埋弧操作、吹氧、喷补炉衬等多项措施,使炉衬寿命稳定在600炉次以上。     

Review of Qualité de vie et drogues. Place aux jeunes.

Reviews the book, Qualité de vie et drogues. Place aux jeunes (1986). In this volume, the author shares his initiatives in the plan of therapeutic and preventive intervention. This book discusses drug use and quality of life in young people. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

提高连续油管使用寿命的方法

从采用软件跟踪疲劳寿命 ,截断法 ,变径连续油管 ,反转使用连续油管 ,防止连续油管损伤 ,合理配置设备 6个方面讨论了控制管串疲劳 ,提高连续油管使用寿命的方法 ,并得出结论 :控制管串疲劳的方法中 ,最有效的方法是实际作业截断法。指出要尽量减少连续油管在带内压下工作 ,也要研究开发降阻性能好的工作液 ,以延长连续油管使用寿命、降低作业风险。     

盛钢桶铝锆碳滑板的研究与生产

通过研究,在盛钢桶用铝锆碳滑板的生产过程中,调整了ZrO2的加入量,添加了复合抗氧化剂,使滑板具用较高的强度和抗氧化性能,提高了滑板的使用寿命.     

Predicting posttraumatic growth in breast cancer survivors.

Wide variability exists with respect to how breast cancer survivors respond to common psychological and psychosocial challenges of their disease, ranging from posttraumatic stress disorder to posttraumatic growth. This cross-sectional study examined contextual, disease-related, and intraindividual predictors of posttraumatic growth in 224 randomly selected breast cancer survivors. A series of hierarchical regression analyses found that age at diagnosis, marital status, employment, education, perceived intensity of disease, and active coping accounted for 34%, 35%, and 28% of the variance in growth in relationships with others, new possibilities, and appreciation for life. These findings suggest that a more comprehensive model of growth will be helpful in understanding the various factors that play a role in breast cancer survivors' perception of psychological and psychosocial growth. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

真丝绸产品的清洁生产与生态设计

通过对真丝绸整个产品生命过程的分析，对其进行了生命周期评价，说明了丝绸与其产地环境之间的联系和影响，尝试寻求两者之间的和谐关系，提出了清洁生产工艺的规划和各种行之有效的对策和措施，尝试了对环境友好的丝绸印染工艺的生态设计。     

Thermomechanical fatigue—damage mechanisms and mechanism-based life prediction methods

An existing extensive database on the isothermal and thermomechanical fatigue behaviour of high-temperature titanium alloy EVII 834 and dispersoid-strengthened aluminum alloy X8019 in SiC particle-reinforced as well as unreinv conditions was used to evaluate both the adaptability of fracture mechanics approaches to TMF and the resulting predictive capabilities of determining material life by crack propagation consideration. Selection of the correct microstructural concepts was emphasised and these concepts were, then adjusted by using data from independent experiments in order to avoid any sort of fitting. It is shown that the cyclic /-integral (δJ_eff concept) is suitable to predict the cyclic lifetime for conditions where the total crack propagation rate is approximately identical to pure fatigue crack growth velocity. In the case that crack propagation is strongly affected by creep, the creep-fatigue damage parameter δ_CF introduced by Riedel can be successfully applied. If environmental effects are very pronounced, the accelerating influence of corrosion on fatigue crack propagation can no longer implicitly be taken into account in the fatigue crack growth law. Instead, a linear combination of the crack growth rate contributions from plain fatigue (determined in vacuum) and from environmental attack is assumed and found to yield a satisfactory prediction, if the relevant corrosion process is taken into account.     

Corrosion fatigue of extruded magnesium alloys

Corrosion fatigue tests were carried out on extruded AZ31 (3% Al, 1% Zn, 0.3% Mn, Mg—the rest), AM50 (5% Al, 0.4% Mn, Mg—the rest) and ZK60 (5% Zn, 0.5% Zr, Mg—the rest) Mg alloys in air, NaCl-based and borate solutions. N_sol/N_air ratios (the relative fatigue life) were used for the analysis of the corrosion fatigue behavior of Mg alloys in various environments, where N_sol and N_air are the numbers of cycles to failure in the solution and in air, respectively. Extruded ZK60 alloy reveals very high fatigue and corrosion fatigue properties in comparison with other alloys. However, it has the lowest relative fatigue life (N_sol/N_air 10⁻³–10⁻²) or the highest sensitivity to the action of NaCl-based solutions in comparison with that of AM50 and AZ31 alloys (N_sol/N_air 10⁻²–10⁻¹). Under the same stress, the corrosion fatigue life of extruded alloys is significantly longer than that of die-cast alloys (N_sol for extruded AM50 in NaCl is two to three times longer than that of die-cast AM50).     

Is the Promissory Note of Personality as Vulnerability to Depression in Default? Reply to Zuroff, Mongrain, and Santor (2004).

In contrast to D. C. Zuroff, M. Mongrain, and D. A. Santor (2004), the current authors find the promissory note of dependency-sociotropy (DEP-SOC) and self-criticism-autonomy (SC-AUT) as a model of risk for depression to be in default. The authors propose reorganizing what has been cast as unitary effort into 3 distinct endeavors: a psychoanalytic clinical theory, development of a refined empirical model of risk for clinical depression, and research examining the effects of DEP-SOC and SC-AUT on interpersonal relationships in nonclinical samples. The authors identify some issues that need to be accommodated regardless of whether the assessment of Zuroff et al. (2004) or their own is accepted. DEP-SOC and SC-AUT are best construed as correlated, continuous dimensions. Future work also needs to accommodate depression as chronic recurrent condition, advances in developmental psychopathology, and more stringent criteria for positing a risk factor for clinical disorder. (PsycINFO Database Record (c) 2010 APA, all rights reserved)